Özet:
In
this thesis, using Ne 28/1 (21 tex) 100% viscose fiber, ring, compact, rotor,
and vortex spinning systems are used to examine the yarns and some selected
properties of knitted fabrics from these yarns. Yarns produced using different
spinning technologies were knitted into a fabric with a plain structure
produced in two different yarn stitch densities (ring and compact are the same,
rotor and vortex are the same). Then, the pilling abrasion (with ICI box and
Martindale) of knitted fabrics produced using yarns from different spinning
technologies and burst strength performance are examined. As a result, the yarn
produced with the compact system in terms of yarn gave the best results of
general properties. Fabrics were examined in two groups, it was observed that
the fabrics knitted with compact yarns had better pilling properties than the
fabrics knitted with ring yarns. However, the pilling performance of knitted
fabric made from yarns produced by vortex technology is better than knitted
fabric from OE rotor yarns.