Structural, Electrical, and Magnetic Properties of the Co-Substituted Bi-2212 System Textured by Laser Floating Zone Technique


Creative Commons License

Ozaslan A., ÖZÇELİK B., Ozkurt B., Sotelo A., Madre M. A.

JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, cilt.27, sa.1, ss.53-59, 2014 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 27 Sayı: 1
  • Basım Tarihi: 2014
  • Doi Numarası: 10.1007/s10948-013-2257-6
  • Dergi Adı: JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.53-59
  • Anahtar Kelimeler: Bi-based cuprates, XRD, SEM, Critical current, M-H, LFZ-technique, SUPERCONDUCTOR COMPOSITES, PHYSICAL-PROPERTIES, PHASE-FORMATION, MICROSTRUCTURE, CERAMICS, BI, RODS, CU, TC, ENHANCEMENT
  • Çukurova Üniversitesi Adresli: Evet

Özet

In this work, Bi2Sr2CaCu2-x Co (x) O (y) (x=0.0, 0.05, 0.10, and 0.25) textured superconductors were prepared by a LFZ melting technique. In all cases, the powder X-ray diffraction patterns of samples show that the Bi-2212 phase is the major one. All samples have good oriented structure, which is a typical picture for superconductors prepared by the LFZ method. Magnetization hysteresis loops, made for all samples at two different temperatures, showed that the loops become narrower with increasing temperature and doping levels. In addition, the effect of Co doping on the critical current density, J (c), of Bi2Sr2CaCu2-x Co (x) O (y) has been estimated from hysteresis loop measurement by using Bean's model. The increase of the Co amount in the Bi2Sr2CaCu2-x Co (x) O (y) structure significantly decreases the critical current density, showing worse connectivity of the grains. All the results indicate that Co substitution for Cu produces the deterioration on the superconducting properties, compared with the undoped samples.

In this work, Bi2Sr2CaCu2-x Co (x) O (y) (x=0.0, 0.05, 0.10, and 0.25) textured superconductors were prepared by a LFZ melting technique. In all cases, the powder X-ray diffraction patterns of samples show that the Bi-2212 phase is the major one. All samples have good oriented structure, which is a typical picture for superconductors prepared by the LFZ method. Magnetization hysteresis loops, made for all samples at two different temperatures, showed that the loops become narrower with increasing temperature and doping levels. In addition, the effect of Co doping on the critical current density, J (c), of Bi2Sr2CaCu2-x Co (x) O (y) has been estimated from hysteresis loop measurement by using Bean's model. The increase of the Co amount in the Bi2Sr2CaCu2-x Co (x) O (y) structure significantly decreases the critical current density, showing worse connectivity of the grains. All the results indicate that Co substitution for Cu produces the deterioration on the superconducting properties, compared with the undoped samples