The effect of the rock type forming the aggregate in lightweight polymer concrete on compressive and flexural tensile strength


KILIÇ A. M., KILIÇ Ö., KESKİN M. Ö.

SCIENTIFIC RESEARCH AND ESSAYS, cilt.5, sa.15, ss.1986-1992, 2010 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 5 Sayı: 15
  • Basım Tarihi: 2010
  • Dergi Adı: SCIENTIFIC RESEARCH AND ESSAYS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.1986-1992
  • Çukurova Üniversitesi Adresli: Evet

Özet

In this study, lightweight polymer concrete samples were produced with limestone (Ceyhan, Adana), pumice (Nevsehir) and zeolite (Gordes, Manisa) as a binder resin, and compressive and flexural tensile strength of these samples were determined via laboratorial experiments. For the study, the cylinder and prismatic samples of polymer on normal aggregate concrete (NAC), polymer on normal and lightweight aggregate mixture concrete (NLAC) and polymer on lightweight aggregate concrete (LWAC) were prepared. The polymer concrete produced was cured 3, 7, 28 and 90 days. The concrete samples were cured at 65% relative humidity with 20 C temperature. The density and slump workability of concrete mixtures were also measured. Laboratory test results showed that lightweight polymer concretes can be produced by the use of limestone, pumice, zeolite and as a binder resin. The use of mixture was recomended due to its satisfactory strength development.