Effect of Na-doping on thermoelectric and magnetic performances of textured Bi2Sr2Co2Oy ceramics


Creative Commons License

KARAKAYA G., ÖZÇELİK B., TORRES M. A., Madre M. A., Sotelo A.

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, vol.38, no.2, pp.515-520, 2018 (SCI-Expanded) identifier identifier

  • Publication Type: Article / Article
  • Volume: 38 Issue: 2
  • Publication Date: 2018
  • Doi Number: 10.1016/j.jeurceramsoc.2017.09.006
  • Journal Name: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
  • Journal Indexes: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Page Numbers: pp.515-520
  • Keywords: Thermoelectrics, Laser processing, Seebeck coefficient, Power factor, Figure of merit, LAYERED COBALTITES, CRYSTAL-STRUCTURE, SUBSTITUTION, CA3CO4O9, POWER, MICROSTRUCTURE, ENHANCEMENT, FABRICATION, GROWTH, PHASE
  • Çukurova University Affiliated: Yes

Abstract

Bi2Sr2,NaxCo2Ox (x = 0.0, 0.025, 0.050, 0.075, 0.100, and 0.125) samples were prepared through the solidstate route and textured using the laser floating zone technique. Microstructural analysis of as-grown samples showed well oriented grains and a relatively high amount of secondary phases due to their incongruent melting. Annealing procedure has drastically decreased the number and amount of secondary phases. Moreover, Nadoping has further decreased the secondary phases content and improved grain alignment. These modifications have been reflected in a large decrease of electrical resistivity with the annealing procedure. The maximum power factor values have been obtained in 0.075 Na-doped annealed samples, 0.20 mW/K(2)m, which are much higher than the best values obtained in textured materials through hot uniaxial pressing. Magnetic properties were very similar for all samples, with paramagnetic Curie temperature and effective magnetic moment values of -48.6 K and approximate to 2 mu(B), respectively.